portland cement-based XPS/EPS Bonding Adhesive Mortar

FOB Reference Price:Get Latest Price
Other300-500 / Bag | 40 Bag/Bags (Min. Order)
Lead Time:
Quantity(Bags) 1 - 1000 >1000
Est. Time(days) 20 Negotiable
Report Suspicious Activity
Overview
Quick Details
Warranty:
Lifetime
After-sale Service:
Online Technical Support
Project Solution Capability:
graphic design
Place of Origin:
Shandong, China
Brand Name:
Biaoyuan
Model Number:
BY628
Type:
Other Heat Insulation Materials
Supply Ability
Supply Ability:
1000 Ton/Tons per Quarter
Packaging & Delivery
Packaging Details
25kg/bag.40kg/bags
Port
Qingdao
Lead Time :
Quantity(Bags) 1 - 1000 >1000
Est. Time(days) 20 To be negotiated

portland cement-based XPS/EPS Bonding Adhesive Mortar

Feature:
1.It has low thermal conductivity and good thermal insulation property that can inhibit the difference in temperature of the wall between summer and winter season effectively.

2.It has good cohesive force and be suitable for different base planes.

3.It has low contraction efficiency that can prevent effectively the cracking and hollowing and avoid forming hot and cold bridge.

4.The construction is convenient and the product can be used after adding water and stirring.

5.It is fire-retardant, non-toxic, environmental and good weather resistance.

6.It if fast drying and drought, has good construction property.
Application:
1.It is suitable for the insulations of various internal and exterior walls and different household floors, basements and heating system, etc.

2.It is suitable for the play mode built-in that can make a protective layer for the EPS.XPS thermal insulation system.
The base materials should be smooth, strong, clean, and dry and non-grease, concrete curing admixture and other loose materials.

Product usage
Depend on the thermal insulation thickness.
Using Methods:
1.Mix thermal insulation glazed hollow bead mortar and water as mixing ratio of 25: (26-5) kg, string completely and standing for 5 minutes, then stir again to get better effect.

2.Plaster the mortar on the wall evenly, leveling with scraper; the thickness of mortar for each time should be about 2 centimeters, and interval is about 24hours.

3.The curing time of thermal insulation glazed hollow bead mortar should be more than 5 days, depending on the thickness and temperature.

4.The insulation layer should be covered by alkali resistant mash cloth and mortar overlay which should use the polymer mortar with good flexibility and excellent water resistance.

Storage Period:
Keep in cold and dry place, unopened product is valid for 1 year.

Spec
25kg/bag

Technical Date:

Thermal conductivity W/(M.K)

≤0.085

Compression strength Mpa

≥0.4

compression-shear strength Mpa

≥50

Linear shrinkage rate %

≤0.3

Dry density /(kg/m³)

301-400